Accreditations and Standards

Proguard Results



AUS/NZ Standards

Standard Description Result
Pull-off Adhesion on Concrete 3.5 Mpa (cohesive failure of concrete)
ISAT : BS1881: Part 208: 1996 Initial Surface Absorption No measurable water flow
ASTM E96-05 Water Vapour Transmission Equivalent Air Layer Thickness (SD) 3m
ASTM E96-05 Water Vapour Transmission Equivalent Air Layer Thickness after 2000 hrs QUV (SD) 3m
AS/NZS 4548.5-1999 Carbon Dioxide Diffusion Coefficient. Equivalent Air Layer Thickness ® 717m
Equivalent Thickness of Concrete (Sc) 179cm
ASTM D4587 Accelerated Weathering - Durability Product maintains coating integrity as described in the table below. QUV / Condensation exposure to 3000 hrs

Australian Standard Description Scale (0-5), 0 being best
AS 1580.481.1.2.1998 Discolouration on pure white 0-1
AS 1580.481.1.3.1998 Degree of Dirt Collection 0
AS 1580.481.1.4.1998 Degree of Dirt Retention 0
AS 1580.481.1.7.1998 Degree of Checking 0
AS 1580.481.1.5.1999 (clause 7.2) Change in Gloss (Visual) 4
AS 1580.481.1.8.1998 Degree of Cracking 0
AS 1580.481.1.9.1998 Degree of Blistering 0
AS 1580.481.1.10.1998 Degree of Flaking & Peeling 0
AS 1580.481.1.11.1998 Degree of Chalking 0
AS 1580.481.1.12.1998 Degree of Colour Change on Pure White 0-1

Pull off Adhesion Results

  • Glass : 4.92 MPa (713 psi) (100% failure of glass)

  • Concrete : 100% failure of concrete. Ranges 1.8 MPa (261 psi) to 8 MPa (1160 psi) depending on the strength of the concrete

  • Glazed Tile : pending

  • Mild Steel (50 micron profile with epoxy zinc primer) : 25.3 MPa (3670 psi)

  • Stainless Steel : 20.3 MPa (2947.5 psi)


ASTM Standards – Tested by KTA Tator

Standard Description Result
ASTM D968-05 Abrasion Resistance by Falling Sand, 100 Litres Max 18.43 L/mil
ASTM D4060-10 Taber Abrasion, 1000g load, CS17 Results Pending
ASTM D1653-12 Water Vapour Transmission - Wet Cup Method approx. 70° Fand 50% Relative Humidity Water Vapour Transmission: 1.393 grains/hr-ft² Water Vapour Permeability: 3.186 perms Permeability: 22.44 perm-mil
ASTM D3273-12 Mould Resistance - Following 500 Hrs Accelerated Weathering No mould growth detected
ASTM D4587-11, Cycle 2 Visual Observations Following 2500 Hrs QUV Exposure Minimal yellowing noted near edges, possibly due to sample racks; No overall change observed in coating condition. No Cracking, Flacking, Peeling, Softening or other defects noted. Colour Retention: ΔE* = 3.35 Gloss Retention: -53%
ASTM D6904-03(13) (TT-C-555B) Wind Driven Rain Resistance (48 Hrs, duplicated determinations) No weight change; No noticeable defects within the coating.
ASTM D7234-12 Tensile Adhesion (Concrete) Results Pending
ASTM D4541-09e1 Tensile Adhesion (Steel) ˃3670 psi
ASTM D4541-09e1 Tensile Adhesion (Stainless Steel) 2947.5 psi

ISO and EN Standards

Standard Description Result
DIN EN 13501-1:201-01 Fire Classification B s1 d0
DIN 53233 Abrasion resistance (falling sand) Rating A
ASTM D 968 (Method A) Abrasion resistance (falling sand) Rating A
DIN EN ISO 2813 Gloss 600 - 57.4
850 - 83.5
DIN EN ISO 11998 Wet Scrub Resistance Class 1 (< 5 um loss after 200 cycles
DIN EN ISO 11998 Cleanability 0 (no perceptible change)
DIN EN 1062-3 Water Permeability 0.025 kg/(m2h0.5) w3 (low)
DIN EN 1542 Adhesive Strength 1.8 – 5.8 MPa (100% cohesive failure of substrate)
DIN EN 13687-1 Freeze / Thaw Cycles (50) with deicing salt immersion 2 MPa (100% cohesive failure of concrete). No cracks, no flakes, no air bubbles, no debonding, no warping. No other surface imperfections.

Fire Classification Table

Class Performance Description Fire Scenario and Heat Attack Examples of Products
A1 No contribution to fire Fully developed fire in a room
/ At least 60kW/m2
Products of natural stone, concrete, bricks, ceramic, glass, steel and many metallic products
A2 No contribution to fire Fully developed fire in a room
/ At least 60kW/m2
Products similar to those of class A1, including small amounts of organic compounds
B Very limited contribution to fire Single burning item in a room
/ 40kW/m2 on a limited area
Gypsum boards with different (thin) surface linings and fire retardant wood products
C Limited contribution to fire Single burning item in a room
/ 40kW/m2 on a limited area
Phenolic foam, gypsum boards with different surface linings (thicker than in Class B)
D Acceptable contribution to fire Single burning item in a room
/ 40kW/m2 on a limited area
Wood products with thickness ≥ about 10mm and density ≥ about 400kg/m³ (depending on end use)
E Acceptable contribution to fire Small flame attack
/ Flame height of 20mm
Low density fibreboard, plastic based insulation products
F No performance requirements Products not tested (no requirements)

Call Nanokote Today

For more information regarding industry standards and accreditations contact Nanokote.


INSTAGRAM

LOCATIONS

AUSTRALIA

6-8 England Street Dandenong
Victoria Australia 3175

Phone: +61 (0) 3 9768 3277

Email: [email protected]

NORTH AMERICA

PO Box 12057,
Dallas, TX 75225-1122 USA

Phone: (844) 855-3345

Email: [email protected]